两种应变强化不锈钢在硫化氢环境下的应力腐蚀开裂行为
- 文件大小:2.86MB
- 浏览次数:
- 发布时间:2014-03-10
文件介绍:
本资料包含pdf文件1个,下载需要1积分
At room temperature and -196 ℃, stress corrosion cracking(SCC) behaviors of S30403 stain- less steel and S31608 stainless steel with different predeformations in acid H2S solution are investigated by slow strain rate test(SSRT) and U -bent specimen test. The result shows that both S30403 stainless steel and S31608 stainless steel are all easy tO' subject to SCC damage in H2S solution, the SCC susceptiv- ities of S30403 stainless steel are higher than these of S31608 stainless steel;with the increase of prede- formations, the SCC susceptivities of these two kinds of stainless steel increase ; these two kinds of stainless steel have lower SCC susceptivities and higher strength at - 196 ℃.用U型试样浸泡试验、慢应变速率拉伸试验,结合腐蚀形貌和断口形貌的扫描电子显微镜观察,在常温和-196℃下,分别研究了不同预变形量的S30403不锈钢和S31608不锈钢在H,s介质中的应力腐蚀开裂(Stresscorrosioncracking,SCC)行为。研究表明:S30403不锈钢和$31608不锈钢在实验溶液中均有较强的SCC敏感性,S30403不锈钢的SCC敏感性高于S31608不锈钢;随着预拉应变量的增大,两种材料的SCC敏感性均呈现增大的趋势。在-196℃下应变强化处理的两种材料在H2S环境中的SCC敏感性低于其在室温应变强化处理时的SCC敏感性,同时表现出更好的抗拉性能。
文件列表
正在加载...请等待或刷新页面...
发表评论
更多..相关推荐
更多..最近更新
- 1现代水晶吊灯(2)
- 2最全CAD快捷键大全全有
- 3SJ/T 10268-1991 电子元器件详细规范 半导体集成电路CF253型低功耗运算放大器
- 4YS/T 606-2006 固化型银导体浆料
- 5关于CL结构体系节能建筑施工技术探究
- 6哈尔滨理工大学校徽ug/nx设计
- 7JB/T 10664-2006 25MW~200MW汽轮机无中心孔转子和主轴锻件 技术条件
- 8施工月报(范本)
- 9工艺布置图CAD图
- 10公共课复习资料
- 11GB/T 32181-2015 轨道交通焊接用铝合金线材
- 12优秀工程造价论文合集50-21
- 13某广场规划设计总平面图(版本8)
- 14HB 1597-1987 连接板
- 15ISO9001-2008 质量管理体系要求