透明亲水丙烯酸树脂防雾材料的制备及研究
- 文件大小:409.58KB
- 浏览次数:
- 发布时间:2014-03-11
文件介绍:
本资料包含pdf文件1个,下载需要1积分
Solution polymerization method was used to prepare hydrophilic anti-fogging acrylate resin.By means of comparison,the optimum synthesis technology conditions was obtained that take ethyl acrylate as soft monomer,methylcrylate was used as hard monomer.The best functional monomers were acrylic acid and ethyl acrylic acid,the accessory functional monomer was β-hydroxyl ethyl acrylate.Cross-linking agent methylol acrylamide belongs to self-cross-linking system.Cross linker was N-hydroxymethyl acrylamide.The quality rate of cross-linking agent and carboxylic acid is 4 to 1.The resin can be cured perfectly at the temperature of 100 ℃ for 40 min.The prepared acrylate resin had excellent water-solubility and anti-fogging character.通过溶液聚合的方法制备了防雾材料亲水丙烯酸树脂。通过试验比较,得到了最佳工艺条件,软单体为丙烯酸乙酯,硬单体为甲基丙烯酸甲酯,官能单体则以丙烯酸、甲基丙烯酸为最佳,辅助官能单体为甲基丙烯酸β-羟乙酯。交联体系采用自交联体系,交联剂采用含有亲水氨基的N-羟甲基丙烯酰胺,交联剂与羧酸质量比为4∶1;交联固化温度100℃,固化时间40min。由此制备的防雾树脂具有优良的水溶性和防雾性。
文件列表
正在加载...请等待或刷新页面...
发表评论
更多..相关推荐
更多..最近更新
- 1SH/T 0211-1998 防锈油脂低温附着性试验法
- 2山东某小区园林绿化工程承包合同
- 3内藏钢支撑剪力墙的混凝土墙板构造CAD图纸
- 4毕业设计建筑部分
- 5工作台stl格式
- 6学生到造价工程师
- 7比较详细的泵房施工图
- 8QJ 2889.12-1997 37°导管连接件 过渡球头型式与尺寸
- 9YJD3-00 4立方米底卸式箕斗图
- 10JC 466-92(96) 砌墙砖检验规则
- 11CB/T 3183-2013 船体结构 型材端部形状
- 12第十章 力法
- 13仪表“死区”对暖通、动力系统的影响
- 142(永久船闸进水前现场交面检查签证实施细则)
- 15(3、4、5、6、7、8) 500kV架空送电线路导、地线设备采购技术条件书