酚醛和丁腈橡胶配比对铝基复合材料用树脂基摩擦材料性能的影响
- 文件大小:565.17KB
- 浏览次数:
- 发布时间:2014-03-14
本资料包含pdf文件1个,下载需要1积分
With cast SiCp reinforced aluminum matrix composites as the dual, the effects of three different ratio between phenolic resin and nitrile on the properties of resin based friction material had been investigated in this paper using MM-1000 friction and wear tester. The results showed that the resin-based friction material had better overall performance when the ratio of phenolic resin and nitrile rubber was 6 : 14, the more stable curve of friction torque, fewer wear loss, fewer abrasive dust and better wear resistance, and when brake pressure was 0.36 MPa, the average friction coefficient was about 0.3, when brake pressure was 0.5 MPa, the average friction coefficient was about 0.27.以铸造SiCp增强铝基复合材料为对偶,采用MM-1000摩擦磨损试验机研究了树脂基中酚醛树脂和丁腈橡胶3种不同配比对摩擦材料性能的影响。结果表明,基体酚醛树脂与丁腈橡胶的配比为6:14、制动压力为0.36MPa时,树脂基摩擦材料平均摩擦因数在0.3左右,制动压力为0.5MPa时,平均摩擦因数在0.27左右,且摩擦扭矩曲线比较平稳,摩擦材料磨损量小,磨擦表面磨屑少,具有较好的耐磨性,其综合性能较好。
- 1济南市写字楼中央空调安装施工组织设计
- 2大楼综合布线系统工程方案书(普天布线)
- 3屋顶花园设计图
- 4QB/T 1474.3-2005 绘图仪尺 比例尺
- 5FZ/T 94061-2012 喷气织机用异形筘气流槽气压值试验方法
- 6公路工程廉政制度29页
- 7电气防火检测合同
- 8测试机SolidWorks设计
- 9服装展位3dsmax设计
- 10DL/T 1611-2016 输电线路铁塔钢管对接焊缝超声波检测与质量评定
- 11HG/T 4405-2012 实心轮胎压力成型机
- 12DB65/T 2137-2004 糖料甜菜纸筒育苗移栽技术规程
- 13DB/T 29-266-2019 天津市钢桥设计标准
- 14DB35/T 882-2009 黑脊倒刺鲃
- 15山东质监站资料员培训讲义