金刚石表面的膜层沉积处理及其感应钎焊的研究
- 文件大小:665.29KB
- 浏览次数:
- 发布时间:2014-03-19
本资料包含pdf文件1个,下载需要1积分
将热丝化学气相沉积(HFCVD)处理的金刚石作为磨料感应钎焊制作金刚石工具。HFCVD处理试验中,混合气为H2和CH4(体积流量比为100∶1.5),炉内压力为2.0kPa,700℃下处理45min后,在金刚石表面沉积了一层非晶碳膜。感应钎焊HFCVD处理的金刚石显示,出露部分的金刚石棱边能保持良好的锋利性;浸没在钎料层下面的金刚石表面形成了有均匀孔隙且形状不规则的铬碳化合物,液态钎料充填这些化合物孔隙之间,能够增强钎料对金刚石的把持强度。3种金刚石磨料感应钎焊制作的金刚石磨盘的高效重负荷石材磨削试验显示,HFCVD处理的金刚石的整体破碎率和脱落率最低。 Diamond grits were deposited by hot filament chemical vapor deposition (HFCVD) and they were used to fabricate the brazed diamond tools by induction brazing. The gas ratio (H2/CH4) used was 100 : 1.5(standard cubic--centimetres per minute), the total gas pressure was maintained at about 2.0 kPa, and the substrate temperature was heated to 700℃ for 45 minutes during HFCVD. As a result, amorphous carbon film is deposited on the diamond surface. The diamond edges exposed out of the filler alloy keeps good sharpness after induction brazing of HFCVD deposited diamond. Chro- mium- carbides with uniform porosity and irregular shapes were formed on the diamond grits im mersed into the brazing filler alloy. The liquid brazing filler metal filled in porosity can enhance the bonding strength between the brazing filler metal and the diamond grits. The heavy--load grinding tests of the brazed diamond wheels fabricated by three kinds of diamond grits show that there is a low percentage of pullout from matrix and whole grain fracture for the deposited diamond grits brazed by induction heating.
- 1污水管道深沟槽大开挖施工方案
- 2祥瑞水木年华湖上项目部卸料平台施工方案
- 3公路质量检测站作业指导书
- 4GA/T 2000.81-2015 公安信息代码 第81部分:案事件相关单位角色代码
- 52012年二级建造师考试市政实务(小抄版)
- 6机械原理牛头刨床课程设计方案Ⅰ的3点和9点
- 7表1.1 岩石边坡开挖单元工程质量评定表(例表)
- 8东方花园A型别墅全套施工图纸
- 9七年级上册英语重点
- 10JG/T 206-2018 外墙外保温用丙烯酸涂料
- 11通用配电设计规范GB50055-93
- 12YB2-200电机零件图
- 13AZ安装工程管道支架重量-计算表(带图表)
- 1496SD469 常用灯具安装图集
- 15“概念设计”与“结构设计”的区别