钛酸钾含量对摩擦片耐摩擦磨损性能的影响
- 文件大小:379.35KB
- 浏览次数:
- 发布时间:2014-03-06
文件介绍:
本资料包含pdf文件1个,下载需要1积分
Flaky potassium titanate were used as stabilizer in the friction materials. A series of friction plates with different content of potassium titanate were prepared. The results showed that all products exhibited good thermal stability and high wear resistance when the content of potassium titanate varied from 3%-53%. The average friction coefficient of friction plates was about 0.29, and wear rates were below 0.38× 10-7 cm3/(N? m).将鳞片状钛酸钾作为摩擦磨损稳定剂用于摩擦材料制造,制备了不同鳞片钛酸钾含量的摩擦材料实验片,并对其进行摩擦磨损性能测试。,结果表明,钛酸钾加入比例为3%~53%时,摩擦片均表现出良好的耐摩擦磨损性和热稳定性,各组实验片平均摩擦因数为0.29,磨损率在0.38×10^-7cm^3/(N?m)以内。
文件列表
正在加载...请等待或刷新页面...
发表评论
更多..相关推荐
更多..最近更新
- 12011二级建造师案例分析6
- 2JJF (京) 3004-2019 数字温湿度计校准规范
- 3公路水泥混凝土路面施工技术规范-JTG-F30-2003
- 4男士休闲皮鞋3dsmax设计
- 5屋面仿古铜瓦施工工法
- 6房地产项目的现场管理
- 7注册建造师执业工程规模标准(矿山工程)
- 8钳子SolidWorks设计
- 9泰锅75T生物燃烧炉施工组织设计
- 102011二级建造师_水利_习题班_第4讲_
- 11武汉某医院病房楼防雷施工方案
- 12DMC48脉冲单机袋式收尘器全套图15张CAD图纸
- 13高炉喷吹煤粉工艺流程图高炉喷吹煤粉工艺流程图
- 14GB/T 18516-2017 便携式油锯 锯切效率和燃油消耗率试验方法 工程法
- 15蓝牙音箱三维模型Rhino犀牛设计3DM格式