车轴钢表面渗氮/渗硫复合层的扭动微动磨损研究
- 文件大小:2.2MB
- 浏览次数:
- 发布时间:2014-03-07
本资料包含pdf文件1个,下载需要1积分
The sulfurized-nitrided layers were prepared on the surface of LZ50 steel by sulfurized-nitri- ded duplex processes. Base on the characterizations of the sulfurized-nitrided layers, the torsional fret- ting wear tests of the sulfurized-nitrided layers and LZS0 steel were carried out in dry condition under different torsional angular displacement amplitudes. The results indicated the sulfurized-nitrided layers were composed of e-Fe2.3 N,γ'-Fe4 N, FeS and FeS2 phases. The fretting regimes of the sulfurized- nitrided layers were changed, i.e. the range of the mixed fretting regime was diminished, and the slip regime shifted to the direction of smaller angular displacement amplitude. The friction torques of the sulfurized-nitrided layers were lower than that of the substrate in the partial slip and slip regimes due to the support of the hard nitrided layer and the lubricating of the sulfide layer. Comparing with the substrate, the wear of material reduced greatly for the sulfurized-nitrided layers. The damage in the partial slip regime was slight, but in the mixed and slip regimes the damage mechanisms of the modified layer were mainly delamination, abrasive wear and oxidative wear.通过对LZ50车轴钢表面进行渗氮/渗硫复合处理,在其表面形成渗氮/渗硫复合层。在对复合层进行表征的基础上,研究了复合层和基体在于态不同角位移幅值下的扭动微动磨损行为。结果表明:渗氮/渗硫复合层由ε―Fe3.3N,γ'-Fe4N,FeS和FeS2相组成;复合层改变了LZ50钢的扭动微动运行区域,使得混合区减小,滑移区向小角位移方向移动;由于高硬度的渗氮层支撑和渗硫层润滑作用,复合层的摩擦扭矩在部分滑移区和滑移区低于LZ50钢;与LZ50钢相比,复合层的磨损程度明显降低,在部分滑移区损伤轻微,在混合区和滑移区,复合层的损伤主要表现为剥层,磨粒磨损和氧化磨损。
- 1砂轮头架三维模型SolidWorksAutoCAD设计
- 2夹具毕业设计全套带图纸-阀盖的加工工艺及夹具设计
- 3常减压装置过气化油管线设置
- 4HJ/T 8.5-1994 环境保护档案管理规范 环境保护仪器设备
- 5LB/T 016-2017 温泉旅游企业星级划分与评定
- 6电气工程常见质量通病及防治措施
- 7全国造价员《建筑装饰工程技术基础知识》
- 8一种超大减速比并自锁减速机
- 9临水施工方案
- 10GB/T 13922.4-1992 水处理设备性能试验除氧器
- 11工程安装材料规格小资料
- 12GB/T 32843-2016 科技资源标识
- 13《民用建筑电气设计规范》
- 141227广东省标准建筑地基基础检测规范(报批稿条文说明)-会议讨论
- 15工程质量安全检测指南2010