轴承钢GCr15的生物油空化腐蚀特性研究
- 文件大小:1.02MB
- 浏览次数:
- 发布时间:2014-03-09
本资料包含pdf文件1个,下载需要1积分
It was studied the cavitation corrosive wear of a GCr 15 bearing steel in a emulsification fuel with 5 wt% biomass oil using a magnetostrictive-induced cavitation vibratory apparatus to simulate the cavitation conditions. The results showed that the cumulative mass loss of bearing materials first increased and then decreased because of the variation of microjet impact as the temperature was increased. The microjet of fuel would cause the biggest impact wear when the fuel temperature was at 45℃. Accordingly, the cumulative mass loss and the cumulative mass loss of bearing material reached their highest values at 45 ℃.以5wt%乳化生物质燃油为空化介质,采用磁致伸缩仪模拟空化条件,探讨了轴承材料(Gcr15)的空化腐蚀磨损特性。结果表明:乳化生物质燃油温度升高时,射流冲击强度先增大后减小,导致轴承材料的累积失重量先增大后减小,在45℃时微射流对材料冲击破坏程度最大.空化与腐蚀磨损的双重作用也达到了最大,轴承材料的累积失重量达到峰值。
- 1DB34/T 1393-2011 定远猪
- 2GD0534-80t-45m门机门座起重机总装图(PDF)
- 3基础强夯处理试验方案内容
- 4jjg(交通)018-1999 滚筒式车速表检验台校准仪检定规程
- 5B型泵图纸
- 6鲁班ET199写狗数据
- 7wkz-0
- 8模具毕业设计全套CAD图纸
- 9DB13/T 1639-2012 地理标志产品清苑熏香
- 10地铁平面规划设计(广州地铁5号线员村站为例)
- 11夹角为75度拦污栅CAD图纸
- 12上海市某高速公路整体施工组织设计
- 13GB/T 34244-2017 液体除菌用过滤芯技术要求
- 14GA 602-2006 干粉灭火装置
- 15JJF 1186-2007 标准物质认定证书和标签内容编写规则