纳米压痕法对304不锈钢残余应力的研究(英文)
- 文件大小:572.63KB
- 浏览次数:
- 发布时间:2014-03-11
本资料包含pdf文件1个,下载需要1积分
The residual stress of the 304 stainless steel was investigated by nanoindentation method.The maximum loads were 500 μN,1 000 μN,1 500 μN,2 000 μN and 2 500 μN respectively.The Suresh theoretical model was used to calculate the residual stress.Results showed that the hardness and elastic modulus of un-annealed stainless steel are constant.The hardness of un-annealed and annealed stainless steel is 5.3 GPa and 4.0 GPa and the elastic modulus are 110 GPa and 100 GPa,respectively.Sink-in phenomenon was found during the indentation experiment based on the Ansys software.The compressive residual stress value in the stainless steel(381 MPa)was observed and calculated by the nanoindentation method,which is in good agreement with the result obtained by the XRD method(350 MPa±23 MPa).This agreement demonstrated the accuracy and reliability of using the nanoindentation method for residual stress study.利用纳米压痕法研究了304不锈钢的残余应力,采用Suresh理论模型恒定载荷时的公式计算残余应力,最大加载载荷依次为500μN、1000μN、1500μN、2000μN、2500μN。结果表明,不锈钢硬度和弹性模量为定值,退火前后的硬度分别为5.3GPa和4.0GPa,弹性模量分别为110GPa和100GPa。利用Ansys分析软件模拟了压痕过程,发现不锈钢在受压过程中有Sink-in现象发生。纳米压痕法测得了未退火不锈钢存在残余压应力,大小为381MPa;用XRD测得了未退火不锈钢中有350MPa±23MPa的残余压应力,两种测量结果吻合良好,说明了纳米压痕法在残余应力测试时的准确性与可靠性。
- 1毕业设计 步进梁式加热炉液压系统设计及改进
- 2锚杆(索)、格构梁技术交底卡
- 3低碳之风活动策划书
- 4地球仪风扇plus inventor设计
- 5装修过来人之经验篇
- 6DB12/T 388-2008 优质小麦栽培技术规范
- 7本田CBX1000摩托车(含CB666引擎)PROE设计
- 8DB50/T 186-2004 玉米自交系 渝3135
- 9贴片机用户手册
- 10选煤厂工程施工组织设计
- 11山东邮政技术中心装饰施工组织设计
- 12GB/T 14914-2006 海滨观测规范
- 13减速器UG课程设计三维模型UG,NX设计
- 14某市科技服务中心中央空调系统设备采购及安装工程投标文件
- 15钢结构设计与计算的基本规定