34CrMo4钢在湿H2S环境下的应力腐蚀试验研究
- 文件大小:300.6KB
- 浏览次数:
- 发布时间:2014-03-11
本资料包含pdf文件1个,下载需要1积分
Stress corrosion cracking properties of 34CrMo4 high - strength steels, the material of com- pressed natural gas vessels in vehicle,were studied. In wet HzS environment,tension tests of compact ten- sion (CT) specimens of 34CrMo4 steel were carried out at the displacement rate of 5 × 10^-5mrn/s. The critical stress intensity factor and crack growth rate were gotten in different concentrations of hydrogen sul- fide solution (20,63,200,630 and 2000 ppm). The results show that Kiscc decreases with increase of the concentrations of hydrogen sulfide, but the influence of the concentration on Ktscc changes very little when hydrogen sulfide concentration reaches a certain value ; da/dt increases with the increase of the concentra- tions of hydrogen sulfide, then while the influence of the concentration on crack growth rate is very little from 630 to 2000 ppm. Key words: compact tension (CT) specimens ; displacement rate ; hydrogen sulfide ; stress corrosion以车载压缩天然气气瓶用钢34CrM04为材料,试样为紧凑拉伸(CT)试样,采用多功能动态应力腐蚀试验机进行恒位移速率拉伸试验,实测了在20,63,200,630和2000ppm的硫化氢水溶液中的应力腐蚀临界应力强度因子KISCC和裂纹扩展速率da/dt。结果表明,应力腐蚀临界应力强度因子‰。。随硫化氢浓度的增大而减小,但当硫化氢浓度达到一定量时,溶液的浓度对KISCC值的影响并不大;裂纹扩展速率da/dt随硫化氢浓度的增大而增大,但在630~2000ppm范围内,硫化氢浓度对裂纹扩展速率影响很小。
- 1冲击钻钻孔灌注桩施工工艺及病害的处理
- 2带冷却段的中密度纤维板连续压机
- 3连接器检测机三维模型SolidWorks设计
- 4HB 6998.5-1994 正弦工具 双正弦电磁吸盘
- 5HB 8033-2002 MJ螺纹六角头阶梯螺栓
- 6简单的边坡放样程序
- 7HB/Z 223. 2-2003 飞机装配工艺 第2部分 螺栓安装
- 810G409预应力管桩
- 9水电站副厂房楼盖设计CAD图纸
- 10JIS C5411-1995 射频同轴电缆用C01型连接器
- 11SB/T 10358-2004 中央储备糖储存库资质条件
- 12阳光花园脚手架施工方案
- 13GB/T 6792-1996 客车车身骨架应力、形变测量方法
- 14京沪高速铁路隧道施工实施细则
- 15理论模拟试题