石墨含量对石墨/铜复合材料载流摩擦磨损性能的影响
- 文件大小:561.17KB
- 浏览次数:
- 发布时间:2014-03-14
本资料包含pdf文件1个,下载需要1积分
The effects of graphite content on current carrying friction and wear behaviors of graphite/copper composites were investigated on a self-made pin-disk tester under different current density with graphite/copper composites and QCr0. 5 as friction pairs. The results show that with the increase of graphite content, the friction coefficient of the compos- ites is reduced, and the current-carrying efficiency and the wear rate are reduced first and then increased. The composites have the best current-carrying efficiency when the graphite weight content is 10%, and the lowest wear rate when the graphite weight content is 12. 5%. With the increasing of current density ,the friction coefficient and current-carrying effi- ciency are reduced, and the wear rate are increased. There are adhesive wear, abrasive wear and arc ablation in the experi- ment, and arc ablation is serious when the current density is large.以石墨/铜复合材料和QCr0.5铜合金为摩擦副,在自制的销盘摩擦磨损试验机上进行不同电流密度下的摩擦磨损试验,考察石墨含量对石墨/铜复合材料载流摩擦磨损性能的影响。结果表职:随着石墨含量的增加,石墨/铜复合材料的摩擦因数下降,载流效率和磨损率先下降后升高,石墨质量分数为10%时,载流效率最高,为12.5%时磨损率最低;随着电流密度的增加,石墨/铜复合材料的摩擦因数和载流效率下降,磨损率逐渐增加;石墨/铜复合材料在载流摩擦过程中存在黏着磨损、磨粒磨损和电弧烧蚀,电流密度较大时,电弧烧蚀比较严重。
- 1DB34/T 124.2-2003 沿江棉花育苗移栽技术规程
- 2钢梁砼柱节点
- 3太园抽水站进水渠施工方案优化
- 4碧水天源别墅(总图)带效果
- 5水云湾基坑支护及土方开挖方案v1.4
- 6马鞍山长江大桥承台配合比实验方案
- 7JIS C 5402-11-14-2006 Connectors for electronic equipment Tests and measurements Part 11-14 Climatic
- 8监理规范对监理月报的要求
- 9XXXXX劳教所道路及其配套工程技术标
- 10头架支架机械制造工艺课程设计
- 11电力宽带网故障解决驱动程序安装手册
- 120030 江西省广丰县某水库除险加固工程施工组织设计
- 13ZY4800-13-25支架随机图册最终
- 14绿化整体资料
- 15大型LNG接收站及码头的消防系统设计方案