钛及其合金的扭动微动摩擦磨损特性
- 文件大小:0.97MB
- 浏览次数:
- 发布时间:2014-03-22
本资料包含pdf文件1个,下载需要1积分
采用新型扭动微动试验机在法向载荷为50、80和110N及角位移幅值为0.3°~10°的条件下进行TA2和TC4合金与ZrO2对磨球的扭动微动试验。在摩擦动力学行为研究的基础上,结合磨痕形貌微观分析,考察TA2和TC4合金的扭动微动磨损特性。结果表明:可用摩擦扭矩―角位移曲线和摩擦扭矩时变曲线表征合金的扭动微动行为,获得了TA2和TC4合金的扭动微动运行工况微动图,TA2合金的混合区较TC4合金的宽。摩擦扭矩随法向载荷和角位移幅值的增加而增加,在相同试验条件下,TA2合金的摩擦扭矩始终大于TC4合金的。在部分滑移区,损伤轻微;在混合区和滑移区,损伤加剧,扭动微动摩擦磨损机制主要为磨粒磨损、氧化磨损和剥落。 The torsional fretting tests of alloys TA2 and TC4 flats against ZrO2 ceramic balls were carried out on a new torsional fretting tester under various angular displacement amplitudes ranging from 0.3° to 10° and imposed normal loads of 50,80 and 110 N.Based on the analysis of the frictional kinetics of the torsional fretting wear and combined with the micro-examinations,the damage characteristics of alloys TC4 and TA2 were also discussed.The results indicate that the behaviors of torsional fretting can be characterized by the curves of friction torque-angular displacement(T-θ) and friction torque curves.Running condition fretting maps of torsional fretting wear for alloys TA2 and TC4 can be set up.The mixed fretting regime of alloy TA2 is wider than that of alloy TC4.The friction torques increase with the increase of the normal loads and angular displacement amplitudes,and alloy TA2 always presents higher friction torques than that of alloy TC4.In the partial slip regime,the damage of torsional fretting wear is slight.In the mixed fretting regime and slip regime,the damage adds,the wear mechanisms of torsional fretting of alloys TC4 and TA2 are mainly abrasive wear,oxidative wear and delamination.
- 1JR/T 0067-2011 证券期货业信息系统安全等级保护测评要求(试行)
- 2最新规范冲刷深度计算
- 3接触开关SolidWorks设计
- 4监理巡视记录
- 5MT 31-1996 煤电钻开关
- 6传动滚筒
- 7沥青路面早期破损及养护
- 8改造工程施工组织设计
- 9AWS B2.1-1-004-2002 在焊接条件下、有或没有垫板、10到18规格的碳钢(M1,组1)的气体保护金属极电弧焊
- 10JB/T 9874-1999 金属切削机床 装配通用技术条件
- 11北京某大学综合游泳馆工程施工组织设计
- 12SJ/T 31228-1994 S7-14LS颚式(玻璃)破碎机完好要求和检查评定方法
- 1302SG614(GJBT-591)框架结构填充小型空心砌块墙体结构构造
- 14防护服一般要求 GB/T 20097-2006
- 15DB14/T 1160-2015 甘薯轻简化栽培技术规程