不同润滑介质下钢一钢摩擦副的摩擦磨损性能
- 文件大小:275.47KB
- 浏览次数:
- 发布时间:2014-03-22
本资料包含pdf文件1个,下载需要1积分
研究了钢一钢摩擦副在干摩擦、水润滑、酒精润滑和60N油润滑等条件下的摩擦磨损行为。结果表明:润滑介质可以显著降低钢-钢摩擦副的摩擦系数,在干摩擦、水润滑、酒精润滑和60N油润滑,摩擦载荷为(50-200)g(铜球半径为2inm)时摩擦系数的平均值分别为0.75-0.81,0.45-0.33,0.22-0.15,0.13-0.09;在高栽荷下酒精润滑与油润滑磨损速率相差甚小,并且在摩擦磨损初期阶段(500S之内)摩擦系数相差甚少;同时,酒精润滑条件下的磨损表面形貌与油润滑下的磨损表面形貌极为相似,无明显粘着现象。分析表明,酒精润滑是一种绿色润滑介质,在压延、拉伸工业中有良好的应用前景。 The friction and wear proPerties of steels-steels friction pairs under dry-friction,water-lu- brication,alcohol-lubrication and 60N oil-lubrication were investigated.The results showed that lubricating medium might decrease signcantly the friction coefficient of the steels-steels friction pairs.When sliding against steel ball(2mm in radius )at the load of(50-200)g under dry-friction condition,water-lubrication, alcohol-lubrication and 60N oil-lubrication,the mean friction coefficients were 0.75-0.81,0.45-0.33,0.22-0.15 and 0.13-0.09,respectively.The mean friction coefficients(within 500s) and spec~c wear rates under alcohol and oil lubrication were almost the same at high load condition.Meanwhile ,the worn tracks seemed very similar,without obvious adhesion.h is believed that alcohol lubrication is a green lubricating medium, which will have a good application prospect in rolling and drawing industries.
- 1建设工程项目监理机构日常工作程序
- 2YBB00242002聚酰胺/铝/聚氯乙烯冷冲压成型固体复合硬片(试行)
- 3桥梁1+1讲堂第二期—李兆阳&刘建华
- 4永磁直线电机气隙磁场几种解析方法的比较
- 5燃气中压管道施工技术要求
- 6XX太阳能电池组件项目(一期)安全文明施工组织设计
- 7由单个气缸带动的直线机械手SolidWorks设计
- 803G101-1混凝土结构施工图平面整体表示方法
- 9GB/T 17917-1999 商场管理信息系统基本功能要求
- 10表H-305
- 11BS EN 10220-2002 无缝钢管
- 12迅雷喊疼工具Thunder5.8.6.607
- 13CNAS-EC-047-2015 基于CNAS-CC170等认可规范调整对ISMS认证机构认可转换的说明
- 14变速器传动机构CAD图纸
- 15005号(三册)岗位安全职责