Influence of Weave Structures on the Tribological Properties of Hybrid Kevlar/PTFE Fabric Composites
- 文件大小:867.68KB
- 浏览次数:
- 发布时间:2014-03-17
本资料包含pdf文件1个,下载需要1积分
The existing research of the woven fabric self-lubricating liner mainly focus on the tribological performance improvements and the service life raised by changing different fiber type combinations, adding additive modification, and performing fiber surface modification. As fabric composites, the weave structures play an important role in the mechanical and tribological performances of the liners. However, hardly any literature is available on the friction and wear behavior of such composites with different weave structures. In this paper, three weave structures (plain, twill 1/3 and satin 8/5) of hybrid Kevlar/PTFE fabric composites are selected and pin-on-flat linear reciprocating wear studies are done on a CETR tester under different pressures and different frequencies. The relationship between the tensile strength and the wear performance are studied. The morphologies of the worn surfaces under the typical test conditions are analyzed by means of scanning electron microscopy (SEM). The analysis results show that at 10 MPa, satin 8/5 performs the best in friction-reduction and antiwear performance, and plain is the worst. At 30 MPa, however, the antiwear performance is reversed and satin 8/5 does not even complete the 2 h wear test at 16 Hz. There is no clear evidence proving that the tensile strength has an influence on the wear performance. So the different tribological performance of the three weave structures of fabric composites may be attributed to the different PTFE proportions in the fabric surface and the different wear mechanisms. The fabric composites are divided into three regions: the lubrication region, the reinforced region and the bonding region. The major mechanisms are fatigue wear and the shear effects of the friction force in the lubrication region. In the reinforced region fiber-matrix de-bonding and fiber breakage are involved. The proposed research proposes a regional wear model and further indicates the wear process and the wear mechanism of fabric composites.
- 1GB 12638-1990 微波和超短波通信设备辐射安全要求
- 2人防建筑图集 07FJ02
- 3水煤浆燃烧器外形图
- 4希顿钢结构施工组织设计(A4版2011.0105)
- 5河南分公司2006年抗震加固监理实施细则(碳纤维加固及坑式静压桩加固)
- 6SC/T 7223.3-2017 黏孢子虫病诊断规程 第3部分:武汉单极虫
- 7含特殊结构机器人的运动学分析
- 8钣金热成形高温模具自动拆装系统的设计原理
- 9NY/T 1930-2010 秸秆颗粒饲料压制机质量评价技术规范
- 10265补强圈试验记录
- 11建筑门窗工艺管理制度
- 12露天储煤场煤堆自燃防治对策
- 13某大桥公路桥桥面拆除实施性施工组织设计
- 14JB/T 9930.5-2015 立式带锯床 第5部分:滑车型立式带锯床技术条件
- 15金桥大道led路灯安装电气工程施工设计方案word文档