橡胶复合料对刹车片性能及表面开裂状态的影响
- 文件大小:4.92MB
- 浏览次数:
- 发布时间:2014-03-23
本资料包含pdf文件1个,下载需要1积分
研究了两种细度的橡胶复合料不同含量时对刹车片摩擦磨损性能和表面开裂状态的影响。实验结果表明,加入一定量橡胶复合料能使刹车片摩擦面产生较少裂纹,有效改善摩擦磨损性能,当含量相同时细度较大的橡胶复合料比细度小的橡胶复合料表面更易开裂、性能更好。综合比较.当橡胶复合料细度较大、含量为20%左右时刹车片表面裂纹适宜具有较好的摩擦磨损性能。 An experimental investigation was carried out to examine the effect of friction and wear property and surface cracking of brake pad with rubber composites at two fineness and different content. Results showed that,adding a certain amount of rubber composites can produce a few cracks in the friction surface, and effectively improve the friction and wear property, rubber composites with bigger fineness have a better performance and the surface is also easier to crack when they have the same content. After the comprehensive comparison, rubber composites got a suitable surface cracks and better wear performance when its fineness is bigger with the content at 20%.
- 1官陡门控制网复测加密技术成果报告
- 2剃须刀三维模型设计
- 3金域华府人工挖孔桩施工方案(正式)
- 4QB/T 2142-2017 玻璃容器 含气饮料瓶
- 5建筑安装速算精品手册
- 62012一级注册建筑师考试模拟试题集(下册-含作图部分)
- 7瓮福大厦幕墙工程专项施工设计方案
- 8GD0528-25t-50m门机门座起重机总装图(PDF)
- 9SJ/Z 9140.4-1987 声系统设备 第10部分 节目电平表
- 10转炉风机报警联锁系统逻辑图
- 11《中华人民共和国招标投标法实施条例》
- 12GB/T 37886-2019 气瓶射频识别(RFID)读写设备技术规范
- 13大面积软土地基基坑格构式加固与开挖技术_pdf
- 14截渗墙工程实例一组6篇
- 15YDT 1731-2008 电信网和互联网灾难备份及恢复实施指南